Tensile
Strength |
Vickers
Hardness (F≥98N) |
Ball
Indentation Diameter |
Brinell
Hardness |
Rockwell
Hardness |
|
|---|---|---|---|---|---|
| N/mm² | HV | mm | HB | HRB | HRC |
| 1430 | 443 | 02.98 | 421 | ||
| 1440 | 446 | 02.97 | 424 | 45 | |
| 1450 | 449 | 02.96 | 427 | ||
| 1455 | 450 | 428 | |||
| 1460 | 452 | 02.95 | 429 | ||
| 1470 | 455 | 02.94 | 432 | ||
| 1480 | 458 | 02.93 | 435 | 46 | |
| 1485 | 460 | 437 | |||
| 1490 | 461 | 02.92 | 438 | ||
| 1500 | 464 | 02.91 | 441 | ||
| 1510 | 467 | 02.90 | 444 | ||
| 1520 | 470 | 02.89 | 447 | ||
| 1530 | 473 | 449 | 47 | ||
| 1540 | 476 | 02.88 | 452 | ||
| 1550 | 479 | 02.87 | 455 | ||
| 1555 | 480 | 456 | |||
| 1560 | 481 | 02.86 | 457 | ||
| 1570 | 484 | 02.85 | 460 | 48 | |
| 1580 | 486 | 462 | |||
| 1590 | 489 | 02.84 | 465 | ||
| 1595 | 490 | 02.83 | 466 | ||
| 1600 | 491 | 467 | |||
| 1610 | 494 | 02.82 | 470 | ||
| 1620 | 497 | 472 | 49 | ||
| 1630 | 500 | 475 | |||
| 1640 | 503 | 02.80 | 478 | ||
| 1650 | 506 | 02.79 | 481 | ||
| 1660 | 509 | 483 | |||
| 1665 | 510 | 02.78 | 482 | ||
| 1670 | 511 | 486 | |||
| 1680 | 514 | 02.77 | 488 | 50 | |
| 1690 | 517 | 02.76 | 491 | ||
| 1700 | 520 | 02.75 | 494 | ||
| 1710 | 522 | 496 | |||
| 1720 | 525 | 02.74 | 499 | ||
| 1730 | 527 | 501 | 51 | ||
| 1740 | 530 | 02.73 | 504 | ||
| 1750 | 533 | 02.72 | 506 | ||
| 1760 | 536 | 02.71 | 509 | ||
| 1770 | 539 | 512 | |||
| 1775 | 540 | 02.70 | 513 | ||
| 1780 | 541 | 514 | |||
| 1790 | 544 | 02.69 | 517 | 52 | |
| 1800 | 547 | 520 | |||
| 1810 | 550 | 02.68 | 523 | ||
| 1820 | 553 | 02.67 | 525 | ||
| 1830 | 556 | 528 | |||
| 1840 | 559 | 02.66 | 531 | ||
| 1845 | 560 | 532 | 53 | ||
| 1850 | 561 | 02.65 | 533 | ||