Tensile
Strength |
Vickers
Hardness (F≥98N) |
Ball
Indentation Diameter |
Brinell
Hardness |
Rockwell
Hardness |
|
|---|---|---|---|---|---|
| N/mm² | HV | mm | HB | HRB | HRC |
| 1860 | 564 | 536 | |||
| 1880 | 570 | 542 | |||
| 1890 | 572 | 02.63 | 543 | ||
| 1900 | 575 | 02.62 | 546 | ||
| 1910 | 578 | 549 | 54 | ||
| 1920 | 580 | 02.61 | 551 | ||
| 1930 | 583 | 02.60 | 554 | ||
| 1940 | 586 | 557 | |||
| 1950 | 589 | 02.59 | 560 | ||
| 1955 | 590 | 561 | |||
| 1960 | 591 | 562 | |||
| 1970 | 594 | 02.58 | 564 | ||
| 1980 | 596 | 567 | 55 | ||
| 1990 | 599 | 02.57 | 569 | ||
| 1995 | 600 | 570 | |||
| 2000 | 602 | 02.56 | 572 | ||
| 2010 | 605 | 575 | |||
| 2020 | 607 | 02.55 | 577 | ||
| 2030 | 610 | 580 | |||
| 2040 | 613 | 02.54 | 582 | ||
| 2050 | 615 | 584 | 56 | ||
| 2060 | 618 | 02.53 | 587 | ||
| 2070 | 620 | 589 | |||
| 2080 | 623 | 02.52 | 592 | ||
| 2090 | 626 | 595 | |||
| 2100 | 629 | 02.51 | 598 | ||
| 2105 | 630 | 599 | |||
| 2110 | 631 | 600 | |||
| 2120 | 634 | 02.50 | 602 | ||
| 2130 | 636 | 604 | |||
| 2140 | 639 | 02.49 | 607 | 57 | |
| 2145 | 640 | 608 | |||
| 2150 | 641 | 609 | |||
| 2160 | 644 | 02.48 | 612 | ||
| 2170 | 647 | 02.47 | 615 | ||
| 2180 | 650 | 618 | |||
| 2190 | 653 | 620 | |||
| 2200 | 655 | 02.46 | 622 | 58 | |
| 675 | 59 | ||||
| 698 | 60 | ||||
| 720 | 61 | ||||
| 745 | 62 | ||||
| 773 | 63 | ||||
| 800 | 64 | ||||
| 829 | 65 | ||||
| 864 | 66 | ||||
| 900 | 67 | ||||
| 940 | 68 | ||||